| Produkt | Description | Application | Viscosity (mPa.s, 25°C) | Epoxy Index (mol/kg) | Hydrolyzable chlorine (%) | Colour (Gardner) | Amine No. (mg KOH/g) | HEW (g/mol) |
|---|---|---|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 10-25 | 7,60-8,10 | max. 0,2 | max.1 | — | — |
| TELALIT® 0343 | Low molecular weight epoxy resin adduct of an aliphatic polyamine | Standard, civil engineering, composites, adhesives | 400-1200 | — | — | — | 850-1200 | Min. 34 |
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | 10-25 | — | — | — | 600-650 | 42 |
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | 5-50 | — | — | — | 1250-1320 | 43 |
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | — | — | — | 550-600 | 49 |
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | 5-50 | — | — | — | 1100-1200 | 50 |
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-10 | — | — | — | 440-490 | 59 |
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-120 | — | — | — | 450-500 | 62 |
| TELALIT® 0642 | Modified cycloaliphatic amine | Construction applications, adhesives and composites. Very fast curing even at low temperatures. | 550-1 050 | — | — | — | 440-490 | 64 |
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | — | — | — | min.290 | 84 |
| TELALIT® 95 | Cycloaliphatic adduct modified | Self-levelling flooring | 110-210 | — | — | — | 300-500 | 95 |
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | — | — | — | 320-350 | 90 |
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | 10-30 | — | — | — | 230-260 | 104 |
| TELALIT® 1203 NF | Cycloaliphatic adduct, modified | For high solid coatings, nonyl phenol free | 50-400 | — | — | — | 250-300 | 120 |
| TELALIT® 3509 IX 50 | Aliphatic adduct modified (substitution for TELALIT® 160) | Lacquers, anticorrosive coatings | 200-700 | — | — | — | 110-135 | 350 |
TELALIT® 2433 VBG 50  | Polyamine adduct modified (substitution for TELALIT® 180) | Waterborne systems | 1 000-2 000 | — | — | — | 130-150 | 243 |
| TELALIT® 3404 X 70 | Polyamide | Anticorrosive coatings, nonylphenol free | 700-2 000 | — | — | — | 145-165 | 340 |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 | max.2 | — | — |
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-10 | 2,94-3,70 | max. 0,1 | max.1 | — | — |
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 6,25-7,15 | max. 0,3 | max.1 | — | — |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 | max.1 | — | — |
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-50 | — | — | — | - | 24 |