Epoxidsysteme für Verbundwerkstoffe


Wicklung & Pultrusion

Produkt KomponentenMischverhältnis (pbw)Tg, DSC (°C)GebrauchsdauerViskosität (mPa.s) Beschreibung
CHS-EPODUR® 520-1687 A/B/C2100/90 /1130-145> 10 h/25°C500-1 000 5 Long pot life, medium viscosity. Curing at higher temperature (at least 80°C).
CHS-EPODUR® 520-1667 A/B/C2100/85/1115-130> 10 h/25°C500-1 000 5 Medium viscosity. Curing at higher temperature (at least 80°C).
CHS-EPODUR® 520-1997 A/B/C3100/95/1165-175> 10 h/25°C1 000-1 200 5 High thermal resistance. Post curing above 160°C.
CHS-EPODUR® 520-1787 A/B/C1/D1100/85/0,5/1085-95> 10 h/25°C1 500-2 000 5 High mechanical properties, long pot life. Curing at higher temperature (at least 80°C).
CHS-EPODUR® 574-0522 A/B100/3085-1001-2 h/25°C200-500 5 Curing at ambient temperature, slow reactivity.

Manuelle Anwendung, Infusions- und Injektionstechnologie, RTM

Produkt KomponentenMischverhältnis (pbw)Tg, DSC (°C)Viskosität (mPa.s)GebrauchsdauerViskosität (mPa.s) Beschreibung
CHS-EPODUR® 582-0512/0492/0502/0482/0590 A/B100/30 (36)90-115 (65)200-400 50,3-4 h/25°C200-400 5 Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion.
CHS-EPODUR® 574-0512/0492/0502/0482/0590 A/B100/28 (34)90-115 (65)350-650 50,3-4 h/25°C350-650 5 Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up.
CHS-EPODUR® 581-0542/0562 A/B100/3280-85200-250 51-2 h/25°C200-250 5 Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades.
CHS-EPODUR® 582-0600 A/B100/37130-150350-550 52-3 h/25°C350-550 5 Slow reactivity, low viscosity, high mechanical properties.
CHS-EPODUR® 582-0420 A/B100/25120-130300-450 50,5-1 h/25°C300-450 5 Medium reactivity, low viscosity, high mechanical properties.
CHS-EPODUR® 619-0600 A/B100/40115-130200-500 52-3 h/25°C200-500 5 Slow reactivity, high mechanical properties. Optimal for hand lay-up.
CHS-EPODUR® 619-0492 A/B100/3280-90200-500 512-30 min/25°C200-500 5 Medium reactivity, high mechanical properties. Optimal for hand lay-up.
CHS-EPODUR® 621-0600 A/B100/40115-130500-800 50,5-1 h/25°C500-800 5 Slow reactivity, high mechanical properties. Optimal for hand lay-up.
CHS-EPODUR® 621-0492 A/B100/3285-100300-500 520-40 min/25°C300-500 5 Medium reactivity, high mechanical properties. Optimal for hand lay-up.
CHS-EPODUR® 520-1787 A/B/C1/D1100/85/0.5/1085-951 500-2 000 5> 10 h/25°C1 500-2 000 5 High mechanical properties, long pot life. Curing at higher temperature (at least 80°C).
CHS-EPODUR® 520-1687 A/B/C2100/90/1130-145500-1 000 5> 10 h/25°C500-1 000 5 Long pot life, low viscosity. Curing at higher temperature (at least 80°C).
CHS-EPODUR® 520-1667 A/B/C2100/85/1115-130500-1 000 5> 10 h/25°C500-1 000 5 Low viscosity. Curing at higher temperature (at least 80°C).
CHS-EPODUR® 520-1997 A/B/C3100/95/1165-1751 000-1 200 5> 10 h/25°C1 000-1 200 5 High thermal resistance. Post curing above 160°C.
CHS-EPODUR® 574-0904 A/B100/5070-801 600-2 200 512-15 min/25°C1 600-2 200 5 Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces.

Prepreg Matrix Systeme

Produkt KomponentenMischverhältnis (pbw)Tg, DSC (°C)Viskosität (mPa.s)Gebrauchsdauer Beschreibung
CHS-EPODUR® 525-0269 A/B/C55100/12/0-3115 – 13514000/23°C 1500/40°C2 – 8 h 12 Solvent-free epoxy prepregging system with chemically induced B-stage, adjustable tack/ drapability. For cold, simple equipped processing. Recommended for general industrial and sport & leisure applications.
CHS-EPODUR® 411-0269 A/B/C55100/9/0-2120 – 1289800/55°C, 2700/70°C0,5 - 2 h 12 Solvent-free epoxy system for hot-melt prepregging, adjustable tack. For industrial and sport & leisure composite applications.
CHS-EPODUR® N 554-0249 A/B/C55100/10/0-3120 – 16510000/40°C 2000/55°C1 - 4 h 12 Solvent-free epoxy system for hot-melt prepregging, adjustable tack/drapability. For applications with higher temperature resistence.

Klebstoffe für Verbundwerkstoffe

Produkt KomponentenMischverhältnis (pbw)Tg, DSC (°C)GebrauchsdauerScherfestigkeit (MPa) Beschreibung
VEROBOND® QUICK A/B100/10050-603 min/25°C/10g10-12 Unique, very fast epoxy adhesive (5 minutes curing time).
VEROBOND® 520-2608 A/B100/14070-8020 min/25°C/50g20-25 Structural adhesive with high elongation up to 55% with excellent peel and shear strength.
VEROBOND® SUPER A/B100/10070-8020 min/25°C/10g20-24 Structural adhesive with high elongation up to 55% with excellent peel and shear strength.
VEROBOND® 14 A/B100/5080-8560 min/25°C/100g20-24 Epoxy adhesive cured at room temperature. Systems is a thixotropic paste of high strength with good chemical resistance.
VEROBOND® 15 A/B100/10060-7025 min/25°C/100g20-24 Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths.
VEROBOND® 531-0903 A/B100/5050-6035 min/25°C/400g15-20 Epoxy adhesive with low viscosity, cured at room temperature. Optimal for chemical anchors.
VEROBOND® 521-0846 A/B100/5060-7028 min/25°C/15g6-8 Two-component epoxy structural adhesive. It is used for structural bonding of a wide range of substrates, especially metals, metal structures, wood and ceramics.