| Product | Description | Components | Mixing Ratio (pbw) | Tg, DSC (°C) | Viscosity (mPa.s) | Pot-life |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 494-1667 | System with medium viscosity cured at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-125 | 500-1 000 5) | — |
| CHS-EPODUR® 520-1687 | Long pot life, medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90 /1 | 130-145 | 500-1 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1667 | Medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | 500-1 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | 1 000-1 200 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0,5/10 | 85-95 | 1 500-2 000 5) | > 10 h/25°C |
| CHS-EPODUR® 574-0522 | Curing at ambient temperature, slow reactivity. | A/B | 100/30 | 85-100 | 200-500 5) | 1-2 h/25°C |
| Product | Description | Components | Mixing Ratio (pbw) | Tg, DSC (°C) | Viscosity (mPa.s) | Pot-life |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0.5/10 | 85-95 | 1 500-2 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1687 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90/1 | 130-145 | 500-1 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1667 | Low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | 500-1 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | 1 000-1 200 5) | > 10 h/25°C |
| CHS-EPODUR® 574-0904 | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. | A/B | 100/50 | 70-80 | 1 600-2 200 5) | 12-15 min/25°C |
| Product | Description | Components | Mixing Ratio (pbw) | Tg, DSC (°C) | Viscosity (mPa.s) | Pot-life |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 525-0269 | Solvent-free epoxy prepregging system with chemically induced B-stage, adjustable tack/ drapability. For cold, simple equipped processing. Recommended for general industrial and sport & leisure applications. | A/B/C55 | 100/12/0-3 | 115 - 135 | 14 000/23°C 1 500/40°C | 2 - 8 h 1)2 |
| CHS-EPODUR® 411-0269 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack. For industrial and sport & leisure composite applications. | A/B/C55 | 100/9/0-2 | 120 - 128 | 9 800/55°C, 2 700/70°C | 0,5 - 2 h 1)2 |
| CHS-EPODUR® N 554-0249 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack/drapability. For applications with higher temperature resistence. | A/B/C55 | 100/10/0-3 | 120 - 165 | 10 000/40°C 2 000/55°C | 1 - 4 h 1)2 |
Product Notes
1) Viscosity of 70% solution in butylglycol/25°C, 2) Viscosity of 40% solution in butylglycol/25°C, 3) In a solution, 4) Recommended mixing ratio with filler, 5) Viscosity at 25°C (Brookfield), 6) System (part A:B) has to be mixed with water in the recommended correct ratio – see Application Sheet, 7) System (part A:B) can be filled with additional filler in the recommended correct ratio – see Application Sheet, 9) Viscosity (Pa.s, 20°C), 11) In time of loading, 12) Depends on technology used
You can also find a comprehensive range of products in the product catalogue (PDF).
If you require detailed product information, please do not hesitate to contact us.