| Product | Description | Application | Viscosity (mPa.s, 25°C) | Amine No. (mg KOH/g) | HEW (g/mol) |
|---|---|---|---|---|---|
| TELALIT® 0343 | Low molecular weight epoxy resin adduct of an aliphatic polyamine | Standard, civil engineering, composites, adhesives | 400-1200 | 850-1200 | Min. 34 |
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | 10-25 | 600-650 | 42 |
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | 5-50 | 1250-1320 | 43 |
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | 550-600 | 49 |
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | 5-50 | 1100-1200 | 50 |
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-10 | 440-490 | 59 |
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-120 | 450-500 | 62 |
| TELALIT® 0642 | Modified cycloaliphatic amine | Construction applications, adhesives and composites. Very fast curing even at low temperatures. | 550-1 051 | 440-490 | 64 |
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | min.290 | 84 |
| TELALIT® 95 | Cycloaliphatic adduct modified | Self-levelling flooring | 110-210 | 300-500 | 95 |
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | 320-350 | 90 |
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | 10-30 | 230-260 | 104 |
| TELALIT® 1203 NF | Cycloaliphatic adduct, modified | For high solid coatings, nonyl phenol free | 50-400 | 250-300 | 120 |
| TELALIT® 3509 IX 50 | Aliphatic adduct modified (substitution for TELALIT® 160) | Lacquers, anticorrosive coatings | 200-700 | 110-135 | 350 |
TELALIT® 2433 VBG 50  | Polyamine adduct modified (substitution for TELALIT® 180) | Waterborne systems | 1 000-2 000 | 130-150 | 243 |
| TELALIT® 3404 X 70 | Polyamide | Anticorrosive coatings, nonylphenol free | 700-2 000 | 145-165 | 340 |
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-50 | — | 24 |
| Product | Description | Application | Viscosity (mPa.s, 25°C) | Epoxy Index (mol/kg) | Hydrolyzable chlorine (%) |
|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 10-25 | 7,60-8,10 | max. 0,2 |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 |
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-10 | 2,94-3,70 | max. 0,1 |
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 7,20-7,70 | max. 0,1 |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 |
Product Notes
1) Viscosity of 70% solution in butylglycol/25°C, 2) Viscosity of 40% solution in butylglycol/25°C, 3) In a solution, 4) Recommended mixing ratio with filler, 5) Viscosity at 25°C (Brookfield), 6) System (part A:B) has to be mixed with water in the recommended correct ratio – see Application Sheet, 7) System (part A:B) can be filled with additional filler in the recommended correct ratio – see Application Sheet, 9) Viscosity (Pa.s, 20°C), 11) In time of loading, 12) Depends on technology used
You can also find a comprehensive range of products in the product catalogue (PDF).
If you require detailed product information, please do not hesitate to contact us.