| Product | Description | Components | Mixing Ratio (pbw) | Tg, DSC (°C) | Viscosity (mPa.s) | Pot-life |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 581-0542/0562 | Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades. | A/B | 100/32 | 80-85 | 200-250 5) | 1-2 h/25°C |
| CHS-EPODUR® 582-0600 | Slow reactivity, low viscosity, high mechanical properties. | A/B | 100/37 | 130-150 | 350-550 5) | 2-3 h/25°C |
| CHS-EPODUR® 582-0420 | Medium reactivity, low viscosity, high mechanical properties. | A/B | 100/25 | 120-130 | 300-450 5) | 0,5-1 h/25°C |
| CHS-EPODUR® 619-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 200-500 5) | 2-3 h/25°C |
| CHS-EPODUR® 619-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 80-90 | 200-500 5) | 12-30 min/25°C |
| CHS-EPODUR® 621-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 500-800 5) | 0,5-1 h/25°C |
| CHS-EPODUR® 621-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 85-100 | 300-500 5) | 20-40 min/25°C |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0.5/10 | 85-95 | 1 500-2 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1687 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90/1 | 130-145 | 500-1 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1667 | Low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | 500-1 000 5) | > 10 h/25°C |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | 1 000-1 200 5) | > 10 h/25°C |
| CHS-EPODUR® 574-0904 | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. | A/B | 100/50 | 70-80 | 1 600-2 200 5) | 12-15 min/25°C |
| CHS-EPODUR® 582-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion. | A/B | 100/30 (36) | 90-115 (65) | 200-400 5) | 0,3-4 h/25°C |
| CHS-EPODUR® 574-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up. | A/B | 100/28 (34) | 90-115 (65) | 350-650 5) | 0,3-4 h/25°C |
Product Notes
1) Viscosity of 70% solution in butylglycol/25°C, 2) Viscosity of 40% solution in butylglycol/25°C, 3) In a solution, 4) Recommended mixing ratio with filler, 5) Viscosity at 25°C (Brookfield), 6) System (part A:B) has to be mixed with water in the recommended correct ratio – see Application Sheet, 7) System (part A:B) can be filled with additional filler in the recommended correct ratio – see Application Sheet, 9) Viscosity (Pa.s, 20°C), 11) In time of loading, 12) Depends on technology used