| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 573 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 8,0-10,5 | 5,3-5,6 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 574 | BPA/F resin modified by difunctional reactive diluent | Composites, civil and electrical engineering, high-solid coatings | 1,4-1,7 | 5,5-5,75 | 174-182 | max. 0,1 | max.100 |
| CHS-EPOXY® 575 | BPA/F resin modified by difunctional reactive diluent | Solventless coatings, penetrants, filled systems, casting applications and insulating materials, high solid coatings | 0,7-0,9 | 5,6-5,9 | 169-179 | max. 0,1 | max.100 |
| CHS-EPOXY® B 201 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone | Prepregs for printed circuits boards, laminates, UV blocking | 1,5-2 | 2,3-2,5 | 400-435 | max. 0,1 | |
| CHS-EPOXY® 514 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,8-1,1 | 5,1-5,4 | 185-196 | max. 0,1 | max.100 |
| CHS-EPOXY® 571 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 6,0-8,0 | 5,4-5,7 | 175-185 | max. 0,03 | max.100 |
| CHS-EPOXY® 572 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 4,5-7,0 | 5,5-5,8 | 172-182 | max. 0,03 | max.100 |
| CHS-EPOXY® 200 M 75 | Solution in methylethylketone | Production of prepreges | 0-2,0 | 1,9-2,3 | 435-525 | max. 0,015 | |
| CHS-EPOXY® 200 M 80 | Solution in methylethylketone | Production of prepreges | 2,5-5,5 | 2,0-2,4 | 410-500 | max. 0,015 | |
| CHS-EPOXY® 520 M 80 | 80% solution in methylethylketone | High solid coatings, prepregs etc. | 0,04-0,05 | 4,1-4,4 //3 | 227-244 //3 | max.300 | |
| CHS-EPOXY® B 200 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone | Prepregs for printed circuits boards, laminates | 1,1-2,3 | 1,8-2,3 | 435-556 | max. 0,1 | |
| CHS-EPOXY® 498 | Epoxy resin modified with mono-functional reactive diluent | Civil engineering, potting and impregnation | 0,5- 0,7 | 4,8-5,1 | 196-208 | max.100 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 573 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 8,0-10,5 | 5,3-5,6 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 574 | BPA/F resin modified by difunctional reactive diluent | Composites, civil and electrical engineering, high-solid coatings | 1,4-1,7 | 5,5-5,75 | 174-182 | max. 0,1 | max.100 |
| CHS-EPOXY® 575 | BPA/F resin modified by difunctional reactive diluent | Solventless coatings, penetrants, filled systems, casting applications and insulating materials, high solid coatings | 0,7-0,9 | 5,6-5,9 | 169-179 | max. 0,1 | max.100 |
| CHS-EPOXY® 514 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,8-1,1 | 5,1-5,4 | 185-196 | max. 0,1 | max.100 |
| CHS-EPOXY® 571 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 6,0-8,0 | 5,4-5,7 | 175-185 | max. 0,03 | max.100 |
| CHS-EPOXY® 572 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 4,5-7,0 | 5,5-5,8 | 172-182 | max. 0,03 | max.100 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Barva (APHA) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® 498 | Epoxy resin modified with mono-functional reactive diluent | Civil engineering, potting and impregnation | 0,5- 0,7 | 4,8-5,1 | 196-208 | max.100 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (Gardner) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 200 M 75 | Solution in methylethylketone | Production of prepreges | 0-2,0 | 1,9-2,3 | 435-525 | max. 0,015 | max.1 |
| CHS-EPOXY® 200 M 80 | Solution in methylethylketone | Production of prepreges | 2,5-5,5 | 2,0-2,4 | 410-500 | max. 0,015 | max.1 |
| CHS-EPOXY® 520 M 80 | 80% solution in methylethylketone | High solid coatings, prepregs etc. | 0,04-0,05 | 4,1-4,4 //3 | 227-244 //3 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (Gardner) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® B 201 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone | Prepregs for printed circuits boards, laminates, UV blocking | 1,5-2 | 2,3-2,5 | 400-435 | max. 0,1 | max.1 |
| CHS-EPOXY® B 200 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone | Prepregs for printed circuits boards, laminates | 1,1-2,3 | 1,8-2,3 | 435-556 | max. 0,1 | max.1 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| CHS-EPOXY® 590 | BPF type | Modifications, adhesives, composites | 3,0-5,5 | 5,70-6,06 | 165-175 | max. 0,03 | max.100 |
| CHS-EPOXY® 301 | BPA type semisolid epoxy resin | Hot casting, solventborne coatings, prepregs | - | 2,7-3,3 | 300-370 | - | |
| CHS-EPOXY® 411 | BPA type semisolid epoxy resin | Hot casting, solventborne coatings, prepregs | 0,5-0,8 //1 | 3,9-4,2 | 238-256 | max.100 | |
ENVIPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| ENVIPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| ENVIPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| ENVIPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| CHS-EPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| CHS-EPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 LA | BPA type with low α-glycol content | Modifications, adhesives, composites | 10,0-12,0 | 5,30-5,50 | 182-189 | max. 0,03 | max.100 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| CHS-EPOXY® 590 | BPF type | Modifications, adhesives, composites | 3,0-5,5 | 5,70-6,06 | 165-175 | max. 0,03 | max.100 |
| CHS-EPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| CHS-EPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 LA | BPA type with low α-glycol content | Modifications, adhesives, composites | 10,0-12,0 | 5,30-5,50 | 182-189 | max. 0,03 | max.100 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Barva (APHA) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® 301 | BPA type semisolid epoxy resin | Hot casting, solventborne coatings, prepregs | - | 2,7-3,3 | 300-370 | - |
| CHS-EPOXY® 411 | BPA type semisolid epoxy resin | Hot casting, solventborne coatings, prepregs | 0,5-0,8 //1 | 3,9-4,2 | 238-256 | max.100 |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (APHA) |
|---|---|---|---|---|---|---|---|
| ENVIPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| ENVIPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| ENVIPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| ENVIPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| Produkt | Popis | Aplikace | Viskozita (mPa) | Epoxidový index | Snadno zmýd. chlor | Barva (Gardner) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | Oct-25 | 7,60-8,10 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 | max.2* |
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-Oct | 2,94-3,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 430 | C8-C10 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 1-Jun | 4,25-4,55 | max. 0,05 | max.1* |
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 6,25-7,15 | max. 0,3 | max.1* |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 | max.1* |
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-Oct | |||
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-100 | |||
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | |||
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | |||
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | Oct-30 | |||
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-Oct | |||
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | Oct-25 | |||
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | May-50 | |||
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | |||
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | May-50 |
| Produkt | Popis | Aplikace | Viskozita (mPa) | Epoxidový index | Snadno zmýd. chlor | Barva (Gardner) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | Oct-25 | 7,60-8,10 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 | max.2* |
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-Oct | 2,94-3,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 430 | C8-C10 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 1-Jun | 4,25-4,55 | max. 0,05 | max.1* |
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 6,25-7,15 | max. 0,3 | max.1* |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 | max.1* |
| Produkt | Popis | Aplikace | Viskozita (mPa) | Aminové číslo | HEW |
|---|---|---|---|---|---|
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-Oct | 440-490 | 59 |
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-100 | 450-500 | 62 |
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | min.290 | 84 |
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | 320-350 | 90 |
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | Oct-30 | 230-260 | 104 |
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-Oct | - | 24 |
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | Oct-25 | 600-650 | 42 |
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | May-50 | 1250-1320 | 43 |
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | 550-600 | 49 |
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | May-50 | 1100-1200 | 50 |
| Produkt | Popis | Komponenty | Mísící poměr | Tg, DSC | Pot-life |
|---|---|---|---|---|---|
| CHS-EPODUR® 561-1557 | Hydrophobic cycloaliphatic epoxy resin and hardener system suitable for outdoor application in severe climatic conditions. Good UV resistance. High Tg. The product complies with the fire safety requirements set out in EN 45545-2. | A/B/C2/D5 | 100/90/0,5/10/390 | 100 - 120 | 1-2 h/60°C |
| CHS-EPOXY® B 201 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone | ||||
| CHS-EPOXY® B 200 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone |
| Produkt | Popis | Aplikace | Viskozita (Pa) | Epoxidový index | EEW | Snadno zmýd. chlor | Barva (Gardner) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® B 201 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone | Prepregs for printed circuits boards, laminates, UV blocking | 1,5-2 | 2,3-2,5 | 400-435 | max. 0,1 | max.1 |
| CHS-EPOXY® B 200 M 80 | 80% solution of brominated (21% wt.) medium molecular weight epoxy resin, dissolved in methyl ethyl ketone | Prepregs for printed circuits boards, laminates | 1,1-2,3 | 1,8-2,3 | 435-556 | max. 0,1 | max.1 |
| Produkt | Popis | Barva (APHA) | Koncentrace | 1,5 Hexadien | Stabilizátor |
|---|---|---|---|---|---|
| Allylchlorid | Čirá kapalina s charakteristickým štiplavým zápachem, extrémně hořlavá, citlivá na UV záření (ztmavne). | < 50 | > 99 | < 0,3 | 0,015-0,025 //11 |
| Produkt | Popis | Barva (APHA) | Koncentrace | 1,5 Hexadien | Stabilizátor |
|---|---|---|---|---|---|
| Allylchlorid | Čirá kapalina s charakteristickým štiplavým zápachem, extrémně hořlavá, citlivá na UV záření (ztmavne). | < 50 | > 99 | < 0,3 | 0,015-0,025 //11 |
| Produkt | Popis | Komponenty | Mísící poměr | Tg, DSC | Pot-life |
|---|---|---|---|---|---|
| CHS-EPODUR® 561-1557 | Hydrophobic cycloaliphatic epoxy resin and hardener system suitable for outdoor application in severe climatic conditions. Good UV resistance. High Tg. The product complies with the fire safety requirements set out in EN 45545-2. | A/B/C2/D5 | 100/90/0,5/10/390 | 100 - 120 | 1-2 h/60°C |
| VEROBOND® QUICK | Unique, very fast epoxy adhesive (5 minutes curing time). | A/B | 100/100 | 50-60 | 3 min/25°C/10g |
| VEROBOND® 520-2608 | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/140 | 70-80 | 20 min/25°C/50g |
| VEROBOND® SUPER | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/100 | 70-80 | 20 min/25°C/10g |
| VEROBOND® 14 | Epoxy adhesive cured at room temperature. Systems is a thixotropic paste of high strength with good chemical resistance. | A/B | 100/50 | 80-85 | 60 min/25°C/100g |
| VEROBOND® 15 | Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths. | A/B | 100/100 | 60-70 | 25 min/25°C/100g |
| VEROBOND® 531-0903 | Epoxy adhesive with low viscosity, cured at room temperature. Optimal for chemical anchors. | A/B | 100/50 | 50-60 | 35 min/25°C/400g |
| VEROBOND® 521-0846 | Two-component epoxy structural adhesive. It is used for structural bonding of a wide range of substrates, especially metals, metal structures, wood and ceramics. | A/B | 100/50 | 60-70 | 28 min/25°C/15g |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0.5/10 | 85-95 | > 10 h/25°C |
| CHS-EPODUR® 520-1687 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90/1 | 130-145 | > 10 h/25°C |
| CHS-EPODUR® 520-1667 | Low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C |
| CHS-EPODUR® 574-0904 | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. | A/B | 100/50 | 70-80 | 12-15 min/25°C |
| CHS-EPODUR® 525-0269 | Solvent-free epoxy prepregging system with chemically induced B-stage, adjustable tack/ drapability. For cold, simple equipped processing. Recommended for general industrial and sport & leisure applications. | A/B/C55 | 100/12/0-3 | 115 – 135 | 2 – 8 h //12 |
| CHS-EPODUR® 411-0269 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack. For industrial and sport & leisure composite applications. | A/B/C55 | 100/9/0-2 | 120 – 128 | 0,5 - 2 h //12 |
| CHS-EPODUR® N 554-0249 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack/drapability. For applications with higher temperature resistence. | A/B/C55 | 100/10/0-3 | 120 – 165 | 1 - 4 h //12 |
| CHS-EPODUR® 574-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up. | A/B | 100/28 (34) | 90-115 (65) | 0,3-4 h/25°C |
| CHS-EPODUR® 581-0542/0562 | Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades. | A/B | 100/32 | 80-85 | 1-2 h/25°C |
| CHS-EPODUR® 582-0600 | Slow reactivity, low viscosity, high mechanical properties. | A/B | 100/37 | 130-150 | 2-3 h/25°C |
| CHS-EPODUR® 582-0420 | Medium reactivity, low viscosity, high mechanical properties. | A/B | 100/25 | 120-130 | 0,5-1 h/25°C |
| CHS-EPODUR® 619-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 2-3 h/25°C |
| CHS-EPODUR® 619-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 80-90 | 12-30 min/25°C |
| CHS-EPODUR® 621-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 0,5-1 h/25°C |
| CHS-EPODUR® 621-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 85-100 | 20-40 min/25°C |
| CHS-EPODUR® 520-1687 | Long pot life, medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90 /1 | 130-145 | > 10 h/25°C |
| CHS-EPODUR® 520-1667 | Medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0,5/10 | 85-95 | > 10 h/25°C |
| CHS-EPODUR® 574-0522 | Curing at ambient temperature, slow reactivity. | A/B | 100/30 | 85-100 | 1-2 h/25°C |
| CHS-EPODUR® 582-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion. | A/B | 100/30 (36) | 90-115 (65) | 0,3-4 h/25°C |
| Produkt | Popis | Komponenty | Mísící poměr | Tg, DSC | Pot-life | Viskozita (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1687 | Long pot life, medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90 /1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1667 | Medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0,5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| CHS-EPODUR® 574-0522 | Curing at ambient temperature, slow reactivity. | A/B | 100/30 | 85-100 | 1-2 h/25°C | 200-500 //5 |
| Produkt | Popis | Komponenty | Mísící poměr | Tg, DSC | Pot-life | Viskozita (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0.5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| CHS-EPODUR® 520-1687 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90/1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1667 | Low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 574-0904 | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. | A/B | 100/50 | 70-80 | 12-15 min/25°C | 1 600-2 200 //5 |
| CHS-EPODUR® 574-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up. | A/B | 100/28 (34) | 90-115 (65) | 0,3-4 h/25°C | 350-650 //5 |
| CHS-EPODUR® 581-0542/0562 | Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades. | A/B | 100/32 | 80-85 | 1-2 h/25°C | 200-250 //5 |
| CHS-EPODUR® 582-0600 | Slow reactivity, low viscosity, high mechanical properties. | A/B | 100/37 | 130-150 | 2-3 h/25°C | 350-550 //5 |
| CHS-EPODUR® 582-0420 | Medium reactivity, low viscosity, high mechanical properties. | A/B | 100/25 | 120-130 | 0,5-1 h/25°C | 300-450 //5 |
| CHS-EPODUR® 619-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 2-3 h/25°C | 200-500 //5 |
| CHS-EPODUR® 619-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 80-90 | 12-30 min/25°C | 200-500 //5 |
| CHS-EPODUR® 621-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 0,5-1 h/25°C | 500-800 //5 |
| CHS-EPODUR® 621-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 85-100 | 20-40 min/25°C | 300-500 //5 |
| CHS-EPODUR® 582-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion. | A/B | 100/30 (36) | 90-115 (65) | 0,3-4 h/25°C | 200-400 //5 |
| Produkt | Popis | Komponenty | Mísící poměr | Tg, DSC | Pot-life |
|---|---|---|---|---|---|
| CHS-EPODUR® 525-0269 | Solvent-free epoxy prepregging system with chemically induced B-stage, adjustable tack/ drapability. For cold, simple equipped processing. Recommended for general industrial and sport & leisure applications. | A/B/C55 | 100/12/0-3 | 115 – 135 | 2 – 8 h //12 |
| CHS-EPODUR® 411-0269 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack. For industrial and sport & leisure composite applications. | A/B/C55 | 100/9/0-2 | 120 – 128 | 0,5 - 2 h //12 |
| CHS-EPODUR® N 554-0249 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack/drapability. For applications with higher temperature resistence. | A/B/C55 | 100/10/0-3 | 120 – 165 | 1 - 4 h //12 |
| Produkt | Popis | Komponenty | Mísící poměr | Tg, DSC | Pot-life | Shear strength |
|---|---|---|---|---|---|---|
| VEROBOND® QUICK | Unique, very fast epoxy adhesive (5 minutes curing time). | A/B | 100/100 | 50-60 | 3 min/25°C/10g | 10-Dec |
| VEROBOND® 520-2608 | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/140 | 70-80 | 20 min/25°C/50g | 20-25 |
| VEROBOND® SUPER | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/100 | 70-80 | 20 min/25°C/10g | 20-24 |
| VEROBOND® 14 | Epoxy adhesive cured at room temperature. Systems is a thixotropic paste of high strength with good chemical resistance. | A/B | 100/50 | 80-85 | 60 min/25°C/100g | 20-24 |
| VEROBOND® 15 | Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths. | A/B | 100/100 | 60-70 | 25 min/25°C/100g | 20-24 |
| VEROBOND® 531-0903 | Epoxy adhesive with low viscosity, cured at room temperature. Optimal for chemical anchors. | A/B | 100/50 | 50-60 | 35 min/25°C/400g | 15-20 |
| VEROBOND® 521-0846 | Two-component epoxy structural adhesive. It is used for structural bonding of a wide range of substrates, especially metals, metal structures, wood and ceramics. | A/B | 100/50 | 60-70 | 28 min/25°C/15g | 6-Aug |
Ucelenou nabídku produktů naleznete také v produktovém katalogu (PDF).
Pokud požadujete podrobné informace o výrobcích, neváhejte nás kontaktovat.